| Material | Aluminium |
| Shape | Round |
| Surface Finish | Coated |
| Grade | Gr1,2,3,4,5,7,9,11,12 |
| Diameter | 2-4500 mm |
| Length | up to 3500mm |
| Material | ALUMINUM |
| Color | Silver |
| Grade | 5454 |
| Shape | Rectangle |
| Surface Treatment | Anodized |
| Technique | Hot Rolled |
| Element | Content (%) |
| Aluminium / Aluminum, Al | 96.3 |
| Magnesium, Mg | 2.7 |
| Chromium, Cr | 0.12 |
| Manganese, Mn | 0.8 |
| Properties | Metric | Imperial |
| Density | 2.6-2.8 g/cm3 | 0.0939-0.1011 lb/in3 |
| Melting point | 607°C | 1125°F |
| Properties | Metric | Imperial |
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Properties | Conditions | ||
| T (ºC) | Treatment | ||
| Thermal conductivity | 134 (W/mK) | 25 | All |
| Material | Aluminium |
| Color | Silver |
| Grade | 2014 |
| Shape | Rectangle |
| Usage/Application | Commercial |
| Anodized | Yes |
| Element | Content (%) |
| Aluminium / Aluminum, Al | 93.5 |
| Copper, Cu | 4.4 |
| Silicon, Si | 0.8 |
| Magnesium, Mg | 0.5 |
| Cromium, Cr | 0.1 (Max) |
| Manganese, Mn | 0.6 |
| Properties | Metric | Imperial |
| Density | 2.8 g/cm3 | 0.1018 lb/in3 |
| Melting point | 510°C | 950°F |
| Properties | Metric | Imperial |
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Properties | Conditions | ||
| T (ºC) | Treatment | ||
| Thermal expansion | 23 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 192 (W/mK) | 25 | O |
| ASTM B210 | ASTM B211 | ASTM B221 | ASTM B241 | ASTM B247 |
| ASTM BB241 | DIN 3.1255 | MIL T-15089 | QQ A-200/2 | QQ A-225/4 |
| QQ A-250/4 | QQ A-367 | SAE J454 |
*Your information is safe with us.
| Thickness | 10 mm |
| Shape | Rectangular |
| Brand | PM |
| Type | Plate |
| Finish | Polished |
| Tensile Strength | 205 Min MPa |
| Material | Aluminum Alloy |
Table 1. Chemical composition for aluminium alloy 6082:
| Element | % Present |
| Si | 0.7-1.3 |
| Fe | 0.0-0.5 |
| Cu | 0.0-0.1 |
| Mn | 0.4-1.0 |
| Mg | 0.6-1.2 |
| Zn | 0.0-0.2 |
| Ti | 0.0-0.1 |
| Cr | 0.0-0.25 |
| Al | Balance |
Table 2 (a). Mechanical properties for aluminium alloy 6082 Soft O:
| BS EN 485-2:2008 Sheet 0.4mm to 6.00mm | |
| Property | Value |
| Proof Stress | 85 Max MPa |
| Tensile Strength | 150 Max MPa |
| Hardness Brinell | 40 HB |
Table 2 (b). Mechanical properties for aluminium alloy 6082 T4:
| BS EN 755-2:2008 Extruded Rod,Bar,Tube & Profiles Up to 200mm Dia.or A/F, Up to 25mm WT tube & Prof | |
| Property | Value |
| Proof Stress | 110 Min MPa |
| Tensile Strength | 205 Min MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 70 HB |
| Elongation A | 14 Min % |
| BS EN 755-2:2008 Rod & Bar Up to 20mm Dia. & A/F | |
| Property | Value |
| Proof Stress | 250 Min MPa |
| Tensile Strength | 295 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 95 HB |
| Elongation A | 8 Min % |
| Material | ALUMINIUM |
| Color | Silver |
| Brand | PM |
| Grade | 6061 |
| Shape | Rectangle |
| Anodized | Yes |
| Component | Amount (wt.%) |
| Aluminium | Balance |
| Magnesium | 0.8-1.2 |
| Silicon | 0.4 – 0.8 |
| Iron | Max. 0.7 |
| Copper | 0.15-0.40 |
| Zinc | Max. 0.25 |
| Titanium | Max. 0.15 |
| Manganese | Max. 0.15 |
| Chromium | 0.04-0.35 |
| Others | 0.05 |
| Temper | Ultimate Tensile Strength (MPa) | 0.2% Proof Stress (MPa) | Brinell Hardness (500kg load, 10mm ball) | Elongation 50mm dia (%) |
| 0 | 110-152 | 65-110 | 30-33 | 14-16 |
| T1 | 180 | 95-96 | 16 | |
| T4 | 179 min | 110 min | ||
| T6 | 260-310 | 240-276 | 95-97 | 9-13 |
| Material | Metal Alloy |
| Color | Silver |
| Grade | HE 30 |
| Shape | Square |
| Usage/Application | Commercial |
| Brand | PM |
| Chemical Composition Limits | |||||||||||
| Weight% | Al | Si | Fe | Cu | Mn | Cr | Mg | Zn | Ti | Other Each | Others Total |
| 6082 | Bal | 0.7 - 1.3 | 0.50 max | 0.10 max | 0.40-1.00 | 0.25 max | 0.06-1.20 | 0.20 max | 0.10 max | 0.05 max | 0.15 max |
| Material | Thickness (mm) | Tensile Strength (N/mm²) min | Yield Strength (N/mm²) min | Elongation on 50mm % (min) |
| Alloy 6082 - T6 Sheet and Plate | 0.2 - 3.0 | 295 | 255 | 8 |
| Alloy 6082 T6 Sheet and Plate | 3.0 - 6.0 | 295 | 240 | 8 |
| Alloy 6082 T6 Sheet and Plate | 6.0 - 25.00 | 295 | 240 | 8 |
| Material | Diameter (mm) | Tensile Strength min (N/mm²) | Yield Strength min (N/mm²) | Elongation on 5.65v % (min) |
| Alloy 6082 T6 Bar | < 20 | 295 | 255 | 8 |
| Alloy 6082 T6 Bar | 20 - 150 | 310 | 270 | 8 |
| Alloy 6082 T6 Bar | 150 - 200 | 280 | 240 | 5 |
*Your information is safe with us.
| Material | Aluminium |
| Color | Silver |
| Shape | Round |
| Diameter | 0.1mm - 3.0mm |
| Surface Finish | Coated |
| Usage/Application | Commercial |
| Material | Aluminium |
| Color | Silver |
| Shape | Round |
| Usage/Application | Commercial |
| Brand | PM |
| Type | Aluminium Sliding Window |
| Material | Aluminium |
| Single Piece Length | 18 meter, 36 meter, 6 meter, 3 meter |
| Shape | Round |
| Brand | PM |
| Color | Silver |
| Is It Anodised | Anodised |
Specifications:
*Your information is safe with us.
| Shape | Rectangular |
| Material | Aluminium |
| Brand | PM |
| Surface Treatment | Mill Finish |
| Color | Silver |
| Finishing | Anodized |
| Minimum Order Quantity | 10 Kilogram |
| Material | Aluminium |
| Grade | 7068 |
| Is It Anodised | Anodised |
| Size | PLATE & ROD |
| Type | Alloy |
| Application | Industrial |
*Your information is safe with us.
| Material | Aluminium |
| Brand | PM |
| Series | 1350 |
| Surface Treatment | Galvanized |
| Application | Commercial |
| Trademark | HAOMEI |
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others-Each | Others Total | Al Min | |
| 1350 | 0.1 | 0.4 | 0.05 | 0.05 | – | 0.01 | 0.05 | – | 0.03 | 0.1 | 99.5 |
| Alloy-Temper | Tensile Strength (ksi) | Yield Strength (ksi) | Elongation (%) |
| 1350-O | 12 | 4 | 34 |
| 1350-H14 | 16 | 14 | 3 |
| 1350-H19 | 27 | 24 | 2 |
| Material | Aluminum |
| Brand | PM |
| Shape | Round |
| Melting Point | 655 Degree C |
| Surface Treatment | Anodized |
| Application | Commercial |
| Chemical Element | % Present |
| Manganese (Mn) | 0.0 - 0.20 |
| Iron (Fe) | 0.0 - 0.70 |
| Copper (Cu) | 0.0 - 0.20 |
| Magnesium (Mg) | 0.50 - 1.10 |
| Silicon (Si) | 0.0 - 0.30 |
| Zinc (Zn) | 0.0 - 0.25 |
| Chromium (Cr) | 0.0 - 0.10 |
| Other (Each) | 0.0 - 0.05 |
| Others (Total) | 0.0 - 0.15 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
| Density | 2.70 g/cm³ |
| Melting Point | 655 °C |
| Thermal Expansion | 23.5 x10^-6 /K |
| Modulus of Elasticity | 69.5 GPa |
| Thermal Conductivity | 201 W/m.K |
| Electrical Resistivity | 0.033 x10^-6 Ω .m |
| Electrical Resistivity | 52 % IACS |
| Mechanical Property | Value |
| Tensile Strength | 145 - 185 MPa |
| Proof Stress | 110 Min MPa |
| Hardness Brinell | 47 HB |
| Material | Aluminium |
| Density | 2.69 g/cm3 |
| Melting Point | 625 Degree C |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 134 W/m.K |
| Thermal Expansion | 25x10-6 /K |
Table 1. Chemical composition for aluminium alloy 5251:
| Property | Value |
| Density | 2.69 g/cm3 |
| Melting Point | 625°C |
| Modulus of Elasticity | 70 GPa |
| Electrical Resistivity | 0.044x10-6 Ω.m |
| Thermal Conductivity | 134 W/m.K |
| Thermal Expansion | 25x10-6 /K |
Table 2 (a). Mechanical properties for aluminium alloy 5251 Soft O:
| BS EN 485-2:2008 Sheet and Plate 0.2mm to 4mm | |
| Property | Value |
| Proof Stress | 170 Min MPa |
| Tensile Strength | 230 - 270 MPa |
| Hardness Brinell | 69 HB |
Table 2 (b). Mechanical properties for aluminium alloy 5251 H22:
| BS EN 485-2:2008 Sheet & Plate 0.2mm to 12.5mm | |
| Property | Value |
| Proof Stress | 140 Min MPa |
| Tensile Strength | 210 - 250 MPa |
| Hardness Brinell | 62 HB |
Specifications:
Table 2 (c). Mechanical properties for aluminium alloy 5251 H24:
| BS EN 485-2:2008 Sheet and Plate 0.2mm to 25mm | |
| Property | Value |
| Proof Stress | 120 Min MPa |
| Tensile Strength | 190 - 230 MPa |
| Hardness Brinell | 56 HB |
Table 2 (d). Mechanical properties for aluminium alloy 5251 H26:
| BS EN 485-2:2008 Sheet and Plate 0.2mm to 50.00mm | |
| Property | Value |
| Proof Stress | 60 Min MPa |
| Tensile Strength | 160 - 200 MPa |
| Hardness Brinell | 44 HB |
Table 3. Physical properties for aluminium alloy 5251:
| Element | % Present |
| Cu | 0.15 |
| Mg | 1.7-2.4 |
| Si | 0.4 |
*Your information is safe with us.
| Material | Aluminium |
| Certification | ASTM, GB/T, EN, ASTMB |
| Color | Silver |
| Length | 100 to 6000mm |
| Trademark | Yong hong |
| Shape | Flat |
Table 1. Chemical composition for aluminium alloy 5083:
| Element | % Present |
| Si | 0.4 |
| Fe | 0.4 |
| Cu | 0.1 |
| Mn | 0.4-1.0 |
| Mg | 4.0-4.9 |
| Zn | 0.25 |
| Ti | 0.15 |
| Cr | 0.05-0.25 |
| Al | Balance |
Table 2 (a). Mechanical properties for aluminium alloy 5083 Soft O/H111:
| BS EN 485-2:2008 Sheet 0.2 - 6.3mm Thick | |
| Property | Value |
| Proof Stress | 125 Min MPa |
| Tensile Strength | 275 - 350 MPa |
| Hardness Brinell | 75 HB |
Table 2 (b). Mechanical properties for aluminium alloy 5083 Soft O/H111:
| BS EN 485-2:2008 Plate 6.3mm to 80mm | |
| Property | Value |
| Proof Stress | 115 Min MPa |
| Tensile Strength | 270 - 345 MPa |
| Hardness Brinell | 75 HB |
Specifications:
Table 2 (c). Mechanical properties for aluminium alloy 5083 Soft O/H111:
| BS EN 485-2:2008 Plate 80mm to 120mm | |
| Property | Value |
| Proof Stress | 110 Min MPa |
| Tensile Strength | 260 Min MPa |
| Hardness Brinell | 70 HB |
| Elongation A | |
| Material | Aluminium |
| Brand | PM |
| Grade | 1000 Series |
| Technique | Extruded |
| Thickness | 0.5- 200 mm |
| Length | Max 11600 mm |
5086 Aluminium have strong corrosion resistance characteristics and high electrical conductivity. These alloys are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F) and tend to lose their strength. They are good low-temperature alloys and gain strength when exposed to subzero temperatures.Aluminium / Aluminum 5086 alloy is a high strength structural alloy. The following data sheet provides an overview of Aluminium / Aluminum 5086 alloy.
| Element | Content (%) |
| Al | 95.4 |
| Mg | 4 |
| Cr | 0.15 |
| Mn | 0.4 |
| Properties | Metric | Imperial |
| Density | 2.65 g/cm3 | 0.0957 lb/in3 |
| Melting point | 588°C | 1090°F |
| Properties | Metric | Imperial |
| Elastic modulus | 70-80 GPa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Properties | Conditions | ||
| T (ºC) | Treatment | ||
| Thermal expansion | 23.9 (10-6/ºC) | 20-100 | - |
| Thermal conductivity | 127 (W/mK) | 25 | All |
| ASTM B209 | ASTM B210 | ASTM B221 | ASTM B241 | ASTM B313 |
| ASTM B345 | ASTM B361 | ASTM B547 | ASTM B548 | MIL C-26094 |
| MIL S-24149/2 | QQ A-200/5 | QQ A-250/7 | SAE J454 | QQ WW-T-700/5 |
| Material | Aluminum |
| Surface | Anodized |
| Shape | Rectangle |
| Finish | Polished |
| Temperatures | 200 and 250 Degree Celcius |
| Electric Fence | White |
5154 Aluminium have strong corrosion resistance. These alloys are sensitive to high temperatures ranging between 200 and 250°C (392 and 482°F), and tend to lose some of their strength. However, the strength of the aluminium / aluminum alloys can be enhanced at subzero temperatures, making them ideal low-temperature alloys.
Chemical Composition:
| Element | Content (%) |
| Aluminium / Aluminum, Al | 96.2 |
| Magnesium, Mg | 3.5 |
| Chromium, Cr | 0.25 |
| Properties | Metric | Imperial |
| Density | 2.66 g/cm3 | 0.3489 lb/in3 |
| Properties | Metric | Imperial |
| Elastic modulus | 70-80 Gpa | 10152-11603 ksi |
| Poisson’s ratio | 0.33 | 0.33 |
| Properties | Metric | Imperial |
| Thermal conductivity (@25ºC/77ºF) | 127 W/mK | 881 BTU in/hr.ft².°F |
| Thermal expansion (@20-100ºC/68-212ºF) | 23.9 x 10-6/ºC | 75x 10-6/ºF |
*Your information is safe with us.
| Material | Aluminium |
| Model | 5754 |
| Color | Silver |
| Finish | Plated |
| Shape | Square |
| Application | Industrial |
| Element | % Present |
| Si | 0.4 |
| Fe | 0.4 |
| Mn | 0.5 |
| Mg | 2.6-3.2 |
| Al | Balance |
| Zn | 0.003 |
| Other | 0.0015 |
| Al | Balance |
| BS EN 485-2:2008 Sheet 0.2mm to 6.00mm | |
| Property | Value |
| Proof Stress | 60 Min MPa |
| Tensile Strength | 160 - 200 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 44 HB |
| BS EN 485-2:2008 Aluminium Sheet 0.2mm to 6.00mm | |
| Property | Value |
| Proof Stress | 80 Min MPa |
| Tensile Strength | 190 - 260 MPa |
| Elongation A50 mm | 12 Min % |
| Hardness Brinell | 52 HB |
| BS EN 485-2:2008 Sheet & Plate 0.2mm to 40mm | |
| Property | Value |
| Proof Stress | 130 Min MPa |
| Tensile Strength | 220 - 270 MPa |
| Elongation A50 mm | 7 Min % |
| Hardness Brinell | 63 HB |
| Material | Aluminium |
| Brand | PM |
| Grade | 2011 |
| Color | Grey |
| Application | Industrial |
| Cross Section | Square |
| Element | % Pre sent |
| Si | 0.004 |
| Fe | 0.007 |
| Cu | 5.0-6.0% |
| Pb | 0.2-0.6% |
| Bi | 0.2-0.6% |
| Zn | 0.003 |
| Other | 0.0015 |
| Al | Balance |
| BS EN 755-2:2008 Rod and Bar Up to 200mm Dia. or 60mm A/F | |
| Property | Value |
| Proof Stress | 125 Min MPa |
| Tensile Strength | 275 Min MPa |
| Elongation A50 mm | 12 min % |
| Hardness Brinell | 95 HB |
| Elongation A | 14 min % |
| BS EN 755-2:2008 Rod and Bar Up to 75mm Dia. | |
| Property | Value |
| Proof Stress | 230 Min MPa |
| Tensile Strength | 310 Min MPa |
| Elongation A50 mm | 6 min % |
| Hardness Brinell | 110 HB |
| Elongation A | 8 min % |
| Property | Value |
| Density | 2.82 kg/m3 |
| Melting Point | 535°C |
| Modulus of Elasticity | 71 GPa |
| Electrical Resistivity | 0.045x10-6 Ω.m |
| Thermal Conductivity | 138 W/m.K |
| Thermal Expansion | 23x10-6 /K |
| Material | Aluminium |
| Color | Silver |
| Shape | Rectangle |
| Finish | Coated |
| Anodized | Yes |
| Application | Industrial |
| Element | Content (%) |
| Aluminium / Aluminum, Al | 93.5 |
| Copper, Cu | 4.4 |
| Magnesium, Mg | 1.5 |
| Manganese, Mn | 0.6 |
| Properties | Metric | Imperial |
| Density | 2.77 g/cm3 | 0.10007 lb/in3 |
| Melting point | 510°C | 950°F |
| Properties | Metric | Imperial |
| Elastic modulus | 70-80 Gpa | 10152-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Properties | Metric | Imperial |
| Thermal expansion (@20-100ºC/68-212ºF) | 22.8 (10-6/ºC) | 12.71 µin/in°F |
| Thermal conductivity (@25ºC/77ºF) | 190 (W/mK) | 1319 BTU in/hr.ft².°F |
| AMS 4037 | AMS 4120 | AMS 4192 | AMS 7223 | ASTM B209 |
| ASTM B210 | ASTM B211 | ASTM B221 | ASTM B241 | ASTM B316 |
| ASTM F467 | ASTM F468 | DIN 3.1355 | MIL B-6812 | QQ A-430 |
| MIL T-50777 | QQ A-200/3 | QQ A-225/6 | QQ A-250/4 | MIL T-15089 |
| SAE J454 | QQ WW-T-700/3 |
*Your information is safe with us.
| Material | Aluminium |
| Grade | 6063 |
| Finish | Coated |
| Application | Industrial |
| Color | Silver |
| Anodized | Yes |
6063 Aluminium is a medium strength alloy commonly referred to as an architectural alloy. It is normally used in intricate extrusions.It has a good surface finish, high corrosion resistance, is readily suited to welding and can be easily anodised. Most commonly available as T6 temper, in the T4 condition it has good formability.
Aluminium alloy 6063 is used in:
| AA6063 | Al Mg0.7Si |
| GS10 | AlMgSi0.5 |
| A-GS | 3.32206 |
| ASTM B210 | ASTM B221 |
| ASTM B241 (Pipe- Seamless) | ASTM B345 (Pipe- Seamless) |
| ASTM B361 | ASTM B429 |
| ASTM B483 | ASTM B491 |
| MIL G-18014 | MIL G-18015 |
| MIL P-25995 | MIL W-85 |
| QQ A-200/9 | SAE J454 |
| UNS A96063 | HE19 |
| Element | 6063 % Present | 6063A % Present |
| Si | 0.2 to 0.6 | 0.3 to 0.6 |
| Fe | 0.0 to 0.35 | 0.15 to 0.35 |
| Cu | 0.0 to 0.1 | 0.1 |
| Mn | 0.0 to 0.1 | 0.15 |
| Mg | 0.45 to 0.9 | 0.6 to 0.9 |
| Zn | 0.0 to 0.1 | 0.0 to 0.15 |
| Ti | 0.0 to 0.1 | 0.1 |
| Cr | 0.1 max | 0.05 |
| Al | Balance | Balance |
Annealed wrought alloyThe most common tempers for 6063 aluminium are:
| BS EN 755-2:2008 Rod & Bar Up to 200mm Dia. | |
| Property | Value |
| Tensile Strength | 130 Max MPa |
| Elongation A50 mm | 16 Min % |
| Hardness Brinell | 25 HB |
| Elongation A | 18 Min % |
| Material | ALUMINUM |
| Grade | 7020 |
| Brand | PM |
| Finish | Coated |
| Anodized | YEs |
| Shape | Rectangle |
The principal alloying ingredients in 7020 Aluminium alloys include manganese, magnesium, copper, zinc and silicon.
| Element | Content (%) |
| Zinc, Zn | 4-5 |
| Magnesium, Mg | 1-1.40 |
| Zirconium, Zr + Titanium, Ti | 0.80 - 0.25 |
| Iron, Fe | 0.4 |
| Silicon, Si | 0.35 |
| Copper, Cu | 0.2 |
| Chromium, Cr | 0.10 - 0.35 |
| Zirconium, Zr | 0.080 - 0.20 |
| Manganese, Mn | 0.050 - 0.50 |
| Other (each) | 0.05 max |
| Other (total) | 0.15 max |
| Aluminum, Al | Remainder |
| Properties | Metric | Imperial |
| Density | 2.78 g/cm³ | 0.100 lb/in³ |
| Properties | Metric | Imperial |
| Tensile strength (@thickness ≤100 mm/≤3.94 in) | ≥ 350 MPa | ≥ 50800 psi |
| Yield strength (@thickness ≤100 mm/≤3.94 in) | ≥ 280 MPa | ≥ 40600 psi |
| Elongation at break (@thickness ≤100 mm/≤3.94 in) | ≥ 10% | ≥ 10% |
| Properties | Metric | Imperial |
| Thermal expansion co-efficient (@20-100°C/68-212°F) | 23.1 µm/m°C | 12.8 µin/in°F |
| Thermal conductivity | 137 W/mK | 951 BTU in/hr.ft².°F |
| Material | Aluminium |
| Brand | PM |
| Shape | Round |
| Finish | Polished |
| Application | Industrial |
| Grade | 7075 |
Aluminum alloys have high strength at subzero temperatures. However, their strength can be reduced at high temperatures.7075 Aluminium alloy is a heat treatable alloy. It has high toughness, strong mechanical strength, and good stress corrosion cracking resistance. The following datasheet gives an overview of Aluminium / Aluminum 7050 alloy.
| Element | Content (%) |
| Aluminum, Al | 89 |
| Copper, Cu | 2.3 |
| Magnesium, Mg | 2.3 |
| Zinc, Zn | 6.2 |
| Zirconium, Zr | 0.12 |
| Properties | Metric | Imperial |
| Density | 2.6-2.8 g/cm3 | 0.0939-0.101 lb/in3 |
| Melting point | 494°C | 920°F |
| Properties | Metric | Imperial |
| Tensile strength | 515 MPa | 74695 psi |
| Yield strength | 455 MPa | 65992 psi |
| Fatigue strength | 240 MPa | 34809 psi |
| Elastic modulus | 70-80 GPa | 10153-11603 ksi |
| Poisson's ratio | 0.33 | 0.33 |
| Elongation | 0.11 | 0.11 |
| Properties | Conditions | |
| T (ºC) | Treatment | |
| Thermal conductivity | 180 W/mK | 25 |
Other designations that are equivalent to Aluminum / Aluminum 7050 alloy include:
*Your information is safe with us.
| Type | Plate |
| Brand | PM |
| Material | Aluminium |
| Is It Anodised | Anodised |
| Thickness | 0.14mm-50.00mm, 0.14mm - 50.00mm |
| Width | 10mm-1800mm |
| Grade | 5000 Series,1000/1060/1050/1100/3003/3105/5083/7068 |
| Temper | O-H112 |
| Material | Aluminium |
| Grade | 2017 |
| Color | Silver |
| Type | Ingot |
| Application | Commercial |
| Finish | Plated |
| Weight% | Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others Each | Other Total |
| 2017 USA | Rem | 0.20-0.8 | 0.7 max | 3.5-4.5 | 0.40-1.0 | 0.40-0.8 | 0.10 max | 0.25 max | 0.15 max | 0.05 max | 0.15 max |
| Weight% | Al | Si | Fe | Cu | Mn | Mg | Cr | Zn | Zr + Ti | Others Each | Other Total |
| 2017A EAA | Rem | 0.20-0.8 | 0.7 max | 3.5-4.5 | 0.40-1.0 | 0.40-1.0 | 0.10 max | 0.25 max | 0.25 max | 0.05 max | 0.15 max |
| Anodised | No |
| Weight | 1 KGS |
| Material | Aluminium Alloy |
| Color | Grey |
| Brand | PM |
| Is It Anodised | Anodised |
*Your information is safe with us.
| Usage | Laboratory |
| Anodised | No |
| Weight | 1 KGS |
| Material | Aluminium Silicon Alloy |
| Grade Standard | Technical Grade |
| Color | Grey |
| Purity | 99.9% |
| Anodised | No |
| Weight | 1 KGS |
| Brand | PM |
| Is It Anodised | Anodised |
| Form | Ingots |
| Material | Aluminium |
| Color | Silver |
| Material | Indium |
| Brand | PM |
| Color | Silver |
| Form | Ingot |
| Shape | Rectangle |
| Application | Industrial |
*Your information is safe with us.
| Material | ALUMINIUM |
| Shape | CIRCLE |
| Color | Silver |
| Brand | PM |
| Width | 90-1200mm |
| Grade | 1000 Series |
| Unit Length | 6 m, 12 m, 18 m, 24m |
| Surface Finish | Anodized |
| Brand | PM |
| Color | Silver |
| Shape | Round |
| Size | 2" |
| Material | Aluminium |
| Material | Aluminium |
| Brand | PM |
| Color | Silver |
| Tolerance | +/- 0.05mm |
| CNC Machining or Not | CNC Machining |
| Type | Shim |
*Your information is safe with us.
| Surface Finish | Electroplated |
| Material | Aluminium |
| Shape | Round |
| Color | Silver |
| Brand | PM |
| Thickness | 0.1 mm to 10 mm |
| Brand | PM |
| Material | Aluminium |
| Usage/Application | Commerical |
| Form | Foil |
| Color | Silver |
| Gsm Microne | 300 |
| Surface Finish | Anodized |
| Hollow Sections | Circular |
| Alloy Or Not | Is Alloy |
| Brand | PM |
| Hardness | Silver |
| Shape | Round |
*Your information is safe with us.
| Surface Finish | Metal Coated |
| Material | Stainless Steel |
| Shape | Round |
| Color | Brown |
| Brand | PM |
| Technique | Hot Rolled |
| Material | Aluminium |
| Brand | PM |
| Color | Silver |
| Shape | Round |
| Alloy | With Alloy |
| Is It Anodized | Anodized |
| Usage/Application | Commercial |
| Material | Lead |
| Shape | Rectangle |
| Color | Silver |
| Weight | 42 KG/ingot |
| Brand | PM |
| Chemical Composition | Sb Sn Zn Fe Cd |